Usporedba strukture ofsetnih ploča i njeno djelovanje na kut vlaženja

Bakula, Ana (2005) Usporedba strukture ofsetnih ploča i njeno djelovanje na kut vlaženja. Diploma work - Pre-Bologna programme. Grafički fakultet. [Mentor: Gojo, Miroslav].

PDF D377_Bakula_Ana.pdf Restricted to Registered users only Download (1MB)

Abstract

Zavisno o koncentraciji otopina za vlaženje određivala su se njihova fizikalno-kemijska svojstva kao što su električna provodnost, pH vrijednost, napetost površine, kontaktni kut i hrapavost te SEM analiza na slobodnim površinama tiskovnih formi za ofsetni tisak. Upotrijebljena su dva uzorka tiskovnih formi s klasičnim diazo kopirnim slojem, te ploča za CTP postupak izrade tiskovne forme koja je razvijana u razvijaču različitih pH vrijednosti. Dobiveni rezultati ukazuju da otopine za vlaženje povećanjem koncentracije smanjuju površinsku napetost, dok električna provodnost uzoraka otopina za vlaženje konstantno raste. Proces vlaženja odvija se u blago kiselom mediju (pH vrijednost iznosi između 5.1 i 4.9, što ukazuje da su u otopinu dodane soli koje djeluju kao puferi. Kontaktni kut, kao mjera dobrog vlaženja, smanjuje se povećanjem koncentracije otopina za vlaženje, omogućujući dobro vlaženje slobodnih površina tiskovne forme. Otopina za vlaženje uspješno djeluje pri koncentraciji već od 30 - 40 vol %. Uzorak 2 pokazuje najbolja svojstva, jer je kontaktni kut dovoljno mali, što ukazuje na dobro razlijevanje otopine za vlaženje po površini tiskovne forme, a time i dobro močenje kao jedan od najvažnijih faktora u plošnom tisku. Razlika u kontaktnom kutu kod uzorka 1 uzrokovana je otapanjem sloja Al2O3 i smanjenjem aktivne površine. Nazočnost površinski aktivnih tvari značajno smanjuje slobodnu površinsku energiju otopina, pa se time smanjuje kontaktni kut mjeren na slobodnim površinama. Kontaktni kut linearno je zavisan o površinskoj napetosti za sve ispitivane uzorke. Linearna zavisnost kontaktnog kuta o površinskoj napetosti ukazuje na dobru kombinaciju svih dodataka u otopinu za vlaženje, prvenstveno površinski aktivnih tvari.

Item Type:	Diploma work - Pre-Bologna programme
Mentor name:	Gojo, Miroslav
Defence date:	2005
Abstract in english:	In dependence of the concentration of the fountain solutions, their physicochemical properties, such as electrical conductivity, pH value, surface tension, contact angle, surface roughness and SEM analyse on nonimage areas of typographical form for offset print were estimated. Two samples of typographical form with clasical diazo coating, and a thermal plate (which was developed in developer widh two diferent pH values), were used. The obtained results show that the surface tension of fountain solution decreases by the concentration of the fountain solution increase, while electrical conductivity for fountain solution samples constantly increases. The dampening process occurs in mild acid medium (pH value is between 5.1 and 4.9), which points out that salts acting as puffera are added to the solution. Contact angle, as a proper moistening measure is being decreased by increasing concentration of fountain solution, enabling good moistening of non-image areas of printing plate. Fountain solution is succesfull at the concentration of 30 – 40%. Sample 2 shows the best properites because the contract angle is small enough, wich indicates good spreading of fountain solutin accross the surface of printing form and good wetting as one of the most important factors in plane printing. The diference in contact angle between sample 1a and sample 1b is coused by melting layer of Al2O3 and decreasing activ surface. Present of surface activ substances decreases surface energy of solvents, wich decreases contract angle measured on non-image areas. Contact angle has lineary dependence on surface tension for all examined samples. Linear dependence of contact angle on surface tension shows that there is a good combination of all fountain solution, most of all surface activ substances.
Uncontrolled Keywords:	Električna provodnost, hrapavost, kontaktni kut, napetost površine, ofsetne ploče, otopina za vlaženje, pH vrijednost površinski aktivne tvari (PAT), SEM analiza
Keywords in english:	Electrical conductivity, roughness, pH value, surface tension, contact angle, offset plates, fountain solution, surface activ substances (SAS), SEM analyse
Subjects:	TECHNICAL SCIENCES > Graphic Technology
Institution:	Grafički fakultet
City:	Zagreb
Number of Pages:	51
Callnumber:	goj 2005 bak
Inventory number:	D377
Status:	Unpublished
Date Deposited:	15 Nov 2013 21:35
Last Modified:	27 May 2014 14:34
URI:	http://eprints.grf.unizg.hr/id/eprint/728

Actions (login required)

View Item